Machining Cast Iron With CBN Inserts

Machining Cast Iron With CBN Inserts

Machining Cast Iron With CBN Inserts

In general terms, the following factors should be considered when applying CBN to an iron component:

Cast iron is not generally very hard (less than HRc.30) but tends to be abrasive. CBN is therefore employed because of its abrasive resistance. Unless the iron has been chilled or deliberately heat treated, the cutting action will be such that the CBN will not be required to anneal the material being cut in the shear zone. Grey cast irons are often fully pearlitic in structure - Grade 14 & 17 are common. In this case, the best results are gained using DR - 100/80 at surface speeds above 400 m/min. if the machine tool or component limit the speed available to less than 400 m/min, DR - 50 becomes more cost effective. Tool life and component quality improvements are often dramatic and more than justify the increased cost of the CBN tools. if the grey cast iron is not fully pearlitic and more free ferrite is present within the structure, the machinability of the iron becomes more difficult to predict. As the level of "soft and sticky" ferrite increases, the tool is more likely to suffer adhesion pick up which will alter the cutting action, resulting in premature wear of the tool. DR-50 becomes more likely to provide good results as the level of free ferrite increases and a short trial will soon determine the most suitable PCBN material.

Fully ferritic grey cast irons are not generally cost effective PCBN applications. S.G. irons are generally soft (less than HRc.30 ) and fully ferritic. PCBN is therefore not generally as efficient as other cuttingtool materials. There has, however, been a tendency to produce S.G. irons (nodular irons) with a pearlitic structure. This has resulted in some nominally S.G. irons machining surprisingly well with PCBN, DR-50 tending to be more successful. Low alloy irons commonly used in the automotive industry can be machined with CBN, but the performance is again dependant on the level of free ferrite in the structure of the iron.

Hardened irons, either heat treated or alloyed and heat treated, are machined in the same manner as hardened steels and are therefore more predictable. Cutting speeds recommended are lower - less than 200 m/min. It must be remembered that cast iron of a given specification produced by a foundry on one day may have a different machinabilty to that produced the next day. Once the benefits of machining with CBN have been determined, it may be considered worthwhile ensuring that castings supplied to the machine shop have a suitable microstructure to guarantee consistent PCBN tool performance. if the structure or grade of cast iron is unknown, a simple trial will soon determine the suitability of PCBN as a cutting tool.

[http://www.pgstools.com] is a carbide insert cutting tool supplier. We offer articles for the purpose of troubleshooting tooling issues. All articles may contain information we have obtained through personal experience as well as reference from suppliers. The information for the article was given thanks to David Richards Engineeringhttp://www.drengus.com

POST COMMENT

Bring Out the Big Guns in Bodrum Justdial arrives at America Effective Titles Get People to Read Before They Leave Ways to Find the Best CD Rates A Useful Guide To Some Common Problems With Tankless Water Heaters Get To Know The Various Types Of Water Heaters The Yoga Belly-Burner Workout - The Flying Locust An Explanation on What are Called Daypacks Custom Belt Buckles for Different Looks How Do You Stop Being Jealous? Facts On You're Expecting Twins Mac book cover Just dialed in